| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2.2 | (Cond.G)g/10min | |
| 熔体流动速率 | ASTM D-1238 | 8.5 | (Cond.L)g/10min | ||
| 物理性能 | 比重 | ASTM D-792 | 1.05 | 23/23℃ | |
| 机械性能 | IZOD冲击强度 | 1/8〃 | ASTM D-256 | 1.8(0.33) | kg.cm/cm(ft.lb/in) |
| 延伸率 | ASTM D-638 | 2.0 | % | ||
| 引张强度 | ASTM D-638 | 550(7810) | kg/cm2(lb/in2) | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 1.7(0.31) | kg.cm/cm(ft.lb/in) | |
| 洛氏硬度 | ASTM D-785 | 82 | M | ||
| 弯曲强度 | ASTM D-790 | 820(11650) | kg/cm2(lb/in2) | ||
| 弯曲弹性率 | ASTM D-790 | 3.3(4.7) | 104kg/cm2(105lb/in2) | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 105(221) | ℃(°F) | |
| 热变形温度 | ASTM D-785 | 86(186) | ℃(°F) | ||
| 燃烧率 | File No E56070 UL&C-CL | 1/16"HB | |||